20RK080取向硅钢

电工钢硅钢片：电工钢钢板经冲片、本地剪切、本地弯曲会引入残余应力，导致磁性能劣化。应力退火（SRA）可以残余应力对磁畴移动与转动的阻碍作用，恢复电磁性能。E.2 在钢板或叠铁心的状态下进行应力退火的注意事项如下。1). 避免氧化和渗碳为了防止氧化应力退火应该在保护气氛下进行，通常是 10％以下氢气（H2）和 90％以上氮气（N2）、本地100％氮气（N2）或者氨分解气氛的非爆炸性保护气氛，露点控制在 0℃以下。冲压加工过程引入的冲压油在退火前应完全去除，防止在退火中发生渗碳，劣化产品磁性。2). 退火温度及保持时间退火温度指材料温度，750℃为宜。为使得钢板各部分退火均匀，需要调整温度与保持时间。温度太低不足以残余应力的影响，温度太高会破坏涂层绝缘性。3). 冷却时间应当避免急剧冷却使材料产生应力应变。冷却时间根据电工钢退火数量进行调整。对于退火小吨位数量时，可按每小时不超过 25℃ 的冷却速度冷却到 350℃,以避免冷却过程中产生应力应变。对于退火大吨位数量时，应采取更加缓慢的冷却速率，以期获得 效果。

电工钢硅钢片：宽度产品的公称宽度 W 范围为 750mm＜W≤1270mm。切边供货的产品母卷宽度允许偏差应为＋00.5mm。用户有特殊要求时，通过协议可以按毛边状态交货，其宽度允许偏差由供需双方通过协议另行约定。7.3.3 镰刀弯产品镰刀弯的检测适用于宽度不小于 150mm 的切边材料，任意 1000mm 长度的产品镰刀弯应不超过0.50mm。供方如能保证，可不进行该试验。7.3.4 不平度和浪高产品不平度的检测适用于宽度不小于 150mm 的材料，其不平度应不超过 1.0％，浪高应不超过 2.5mm。7.3.5 残余曲率根据需方要求，并在合同中注明，宽度不小于 150mm 的产品可检测残余曲率，其测试钢片的底边和支撑板间的距离应不超过 10mm。供方如能保证，可不进行该试验。7.3.6 毛刺高度切边产品的剪切毛刺高度应不超过 0.020mm。

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Since it is a functional material, its performance testing also revolves around "function". These indicators are often mentioned in trade and processing processes, and a brief understanding can help everyone better carry out their work. The performance testing of electrical steel mainly includes the following aspects: magnetic inspection, stacking coefficient inspection, coating adhesion inspection, repeated bending inspection, size and shape surface inspection, and conventional mechanical property inspection. In addition to the types of products listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, which are used as intermediate and intermediate grade High frequency motors and transformers, as well as pulse transformers, etc； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding. Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength. Magnetic induction strength is the number of magnetic lines passing through a unit cross-sectional area of the iron core, also known as magnetic flux density. It represents the material‘s magnetization ability, measured in T. The magnetic induction strength of electrical steel plates is high, and the excitation current (also known as no-load current) of the iron core is reduced. Copper and iron losses are also reduced, which can save electrical energy. When the power of the motor and transformer remains constant, the magnetic induction intensity is high, and the design Bm can be increased. The cross-sectional area of the iron core can be reduced, which reduces the volume and weight of the iron core, and saves the amount of electrical steel plates, wires, insulation materials, and structural materials used. This can reduce the total loss and manufacturing cost of the motor and transformer, and is beneficial for the manufacturing, installation, and transportation of large transformers and motors. The main requirements for the performance of silicon steel are: 1. Low iron loss is the most important indicator of the quality of silicon steel sheets. Various countries classify grades based on iron loss values, with the lower the iron loss, the higher the grade. 2. Under strong magnetic fields, the magnetic induction intensity (magnetic induction) is high, which reduces the volume and weight of the iron core of the motor and transformer, saving silicon steel sheets, copper wires, and insulation materials. 3. The surface is smooth, flat, and the thickness is uniform, which can improve the filling coefficient of the iron core. 4. Good lamination performance is more important for manufacturing micro and small electric motors. 5. The adhesion and weldability of the surface insulation film are good, which can prevent corrosion and improve the punching performan